Seeking source for PECVD R&D Tungsten Coatings from WF6. Regards, Frank D. Frank Bazzarre Axic Inc. 493 Gianni St. Santa Clara, CA 95054 Phone 408-980-0240 Fax...
Frank Bazzarre
frank@...
Oct 20, 2009 9:54 pm
5628
With proper cooling you should be able to increase power well over 25 watts. The manufacturer of the sputter source might have some pertinent data for that...
Dear new member, We can help you make a start in this business. Hauzer techno Coating offers high tech Arc Evaporation, and Sputtering Technolgy. Pattents for...
ATL offers Conventional CVD tungsten coating services. We have deposited tungsten and tugsten carbide on a wide variety of substrates for many different...
Hi Shoaib, Few suggestions when you are trying to do cathodic arc deposition: Use a conical shaped graphite target instead of circular. Possibly use a smaller...
Dear Zafar Iqbal Graphite coating is possible by ARC technology. We offer this technology to the market. See www.hauzer.nl Best regards from netherlands Lucien...
we have a coating machine. coating height 240 mm.it's rod feed & curciable based machine. titanium eveporation by ion bombardment. during coating mode machine...
Dear Vasco, May I inform you that my colleague Prof. Janos Labar developed a program "ProcessDiffraction" which helps the evaluation of the selected area ...
Vasco Teixeira
vasco@...
Oct 29, 2009 12:20 am
5636
Dear Jonaid, For surgical instruments and othopedic implants you will need biocompatible coating. TiN is famous but the oldest if you compare with other...
Dear Luciwn Peeters Thanks for the offer Graphite coating by pure arc is not possible. One has to use magnets beneath the target to steer the arc. I am looking...
From: AVS Short Course Announcement [mailto:course_announcement@...] Sent: Tuesday, October 20, 2009 10:30 AM To: AVS Short Course Announcement Subject:...
The one week course in all aspects of optical thin films: DESIGN AND PRODUCTION OF OPTICAL THIN FILMS by Ron Willey will be presented 1-5 February 2010 in...
Ron Willey
Ron@...
Oct 29, 2009 12:22 am
5640
Dear New Member, IonBond is the global leader in the coating of surgical instruments and implants. We have extensive experience in the coating of all ...
Fontana, Ray
r.fontana@...
Oct 29, 2009 12:23 am
5641
To bond the target on the backing plate, both target and backing plate are heated with Indium in between. Do you think the target becomes non-magnetic...
Manoj, I would the following procedure to heat up the FeCrAlY above the Curie temperature during sputtering 1) Use the a few short graphite core from the...
What is the vacuum level before the first level and the same for the second level? Do you have a RGA to scan the system, pre and post? Best regards, Dan In a...
Dear Pramod, I suppose magnetic properties return after cooling. The temperature should be high during sputtering. This could perhaps be achieved by adjusting...
dear Mr. Iqbal, You are right. We can help you build such a system which can be used for both cathodic arc and sputtering. Regards H.R. Prabhakara ... From:...
Hello there I am looking for a second hand arc coating machine which can coat inside ID of the Al extrusion die. Any reference for research paper will be...
Manoj, Please check for vacuum leaks using a good leak detector. Moisture can kill the coating. Contact my friend Dr. Sanjay Patil at H. Fullinger in Pune. ...
Dear Colleges Is anybody knows suppliers for: 1- A high intensity UV light source with two different wavelengths for microscopic glass slides illumination. 2-...
sodky abolila
abo_95@...
Nov 1, 2009 11:07 pm
5650
Dear Minoj, Do you use pre-cleaning of your job before coating. There are many causes of poor color and adhesion. Mention the material of work piece and also...
I need help because I have funds for a postdoc position but unfortunately, the candidate who should come...will not !!! So I send to all of the group subject...
corinne.nouveau@...
Nov 1, 2009 11:08 pm
5652
WHAT IS THE DIAM OF THE TUBE Marion [Non-text portions of this message have been removed]...
Galco123@...
Nov 3, 2009 11:31 am
5653
Dear colleagues, Following my last email, here is the subject of the postdoctoral position for which we should find a candidate for next Sunday !!:...
corinne.nouveau@...
Nov 3, 2009 11:32 am
5654
vacuum level 1.8* 10-3 both lower and upper level.( during coating mode) process starting vacuum level is 4* 10-5. I don't know about RGA. thanks & regards ...
we are use pure titanium pallet. work piece material mainly HSS, CARBIDE OR D2 Etc. for pre-cleaning we have 2 steps 1. hydro-carbon based ultra-sonic...
Hi: Can't help with a machine, but a reference to inside coatings using vacuum arc deposition can be found in R.L. Boxman, S. Goldsmith, S. Shalev, H. Yaloz...