Dear collegues, This is a quick note to inform you all that the initial list of invited lectures for the "International Conference on Surfaces, Coatings and...
Dear Colleagues, If there is anyone who is interested in sponsoring the INTERNATIONAL CONFERENCE ON SURFACES, COATINGS AND NANOSTRUCTURED MATERIALS, which is...
Dear all, I am looking for suppliers of both IVD- Al PVD and Zn EB-PVD coatings. Please, may you give me any indications? Thank youi in advance and best...
Can anyone give me a list of (international) vendors who have the capability to coat large specimens (say up to 6 feet in length) and at least a few in a...
Klingenberg, Melissa L
klingenb@...
Nov 3, 2004 10:54 am
1335
Dear Talek, Just check the density, which is evidently higher for Zirconium (~6,5g/cm3) than for Titanium (~4,5g/cm3). Regards, Witold ...
Gulbinski
gulbinsk@...
Nov 3, 2004 11:43 pm
1336
If you do not have access to X-ray analysis, by weight you can do it. Titanium is lighter than Zirconium. Ti density 4.54gms/cc Zr density 6.506gms/cc. Best...
DAR1SCM@...
Nov 3, 2004 11:44 pm
1337
Melissa, At which CTC facility are you located? If you happen to be in the Washington DC/MD/NoVA area, it may make sense for you to work with my company,...
Roberta, We do IVD aluminum on non-complex geometries (i.e., not on internal diameters), but we are a consulting firm, not a job shop. What is your...
Klingenberg, Melissa L
klingenb@...
Nov 4, 2004 12:04 am
1339
Dear Melissa We have expertise in the manufacture of big vacuum coaters (for substrates up to 16 m long). Please contact our USA representative Eduard...
Vitali Verigin
coatinfo@...
Nov 4, 2004 12:04 am
1340
Roberta, Large and very reputable supplier of both IVD and EB-PVD is Cametoid Limited, Whitby, Ontario, Canada. Contact Claude Lavoie, President ...
Hi Melissa, IonEdge Corporation has the process that you are looking for. The focus of our research for the past decade has been to develop large area-high ...
Mandar Sunthankar
mandar@...
Nov 4, 2004 12:05 am
1342
Are you looking for a subcontractor for EB-PVD or a supplier for equipment? Please let me have info on substrates, size, material ,qt., as well as on coating...
Angel Hershko
angel@...
Nov 4, 2004 12:05 am
1343
Hello Melissa, We at VST Service Ltd. Would like to offer you the PVD system you need. I would require as a first step some data on the substrate nature, shape...
Angel Hershko
angel@...
Nov 4, 2004 12:05 am
1344
Dear members I am currently trying to develop an FCVA (Filtered Cathode Vacuum Arc) to investigate ta-C films, using a pulsed power supply. However, I have no ...
Francisco das Chagas...
marques@...
Nov 4, 2004 4:08 pm
1345
Dear All, I am looking information about developments in the field of in-line continuous PVD process for anti-wear coatings mass production: publications,...
ROSTAGNO Maddalena
maddalena.rostagno@...
Nov 4, 2004 4:10 pm
1346
We are attempting to produce a brassy gold appearance on a piece of clear acrylic by evaporation metalizing the back of the part with aluminum bronze. Thus far...
We are using Alumet 1400/1900 in our plant. Try using Copper aluminum, I have done that very long ago also Metalising in the back on PC lens with good result....
Dear Francisco For general PVD technology and cathodic arc deposition I can recomend you to try the following books (both from our colleagues in this PVD...
Vasco Teixeira
vasco@...
Nov 6, 2004 12:58 am
1349
Dear members: I am looking for a process to deposit mold-releasing layers on the WC mold used in the glass molding process. The mold temperature is around...
hong
hong@...
Nov 6, 2004 11:12 pm
1350
Dear Chad, The problem is that Al has higher evaporation temperature than the Cu. Try explosive evaporation to overcame the problem. It will be better to...
Dear Franklin, please try TiAlN e. g. 50:50. It should work up to 800°C. Maybe you contact Dr. J. F. Chang TEL: 886-6-5051688 Fax: 886-6-5051288 Add: No. 96,...
Dear Franklin, In case the moulds work in protective atmosphere (nitrogen in your case), you can try coating them with thin MoS2 film. In air MoS2 oxidizes at...
To all PVD_coatings members, I am finishing my PhD in surface engineering in Melbourne, Australia. I have a Bachelor with honours degree in Materials Science...
Chad, The effect you are looking for can be easily achieved in a continuous roll to roll system. Welding Alloys Group offer a special aluminium/copper alloy...
Roger SA Kelly
roger.kelly@...
Nov 9, 2004 12:12 am
1356
Dear Dr. Hong: I have made some tests with AlTiN Saturn from Metaplas. The tests were on cobalt substrate at 750°C and the results were almost 100%...
Sadosa
sadosa@...
Nov 9, 2004 12:12 am
1357
Dr. Hong, I asked the PVD Forum a similar question a while back. Here are some of the suggestions I received. I would suggest you start with TiAlN. It...
Dear Porfessor Hong: I suggest the non-sticking hard coating, including graded CrN, multilayered TiAlN, and AlTiN, for the glass molding process. All the above...
Dear all, We proposed the application of a Niobium compound, a brazilian technique, with succes to GENTEX, Co.(cf. Mr. Don Flowers}. Further details, see the ...