... Thanks again, Don Mattox ____________________________________ Donald M. Mattox Technical Director Society of Vacuum Coaters 71 Pinon Hill Place NE ...
SVC
donmattox@...
Dec 1, 2005 10:28 am
2522
Base pressure of the order of 6X10(-5) is ok for a diff+rot pumps combination.Still lower limit could be improved by baking the system.Likely source could be...
What is the chamber material type? Did your coolant have any additives? Soat up as much as possible, use proper towels, wipe with IPA, warm up the base with a...
Hi sammy, As already mentioned it is important to remove as much of the water as possible. Personally, I have used repeated applications of IPA with good...
Hello! I am interested to coat iron substrates with an aluminum oxide dense coating some 3-10 microns thick, to obtain good electrical insulation and good...
thanks Ian and everyone who has give me some ideas.. it really does help me decide what's best based on your suggestion. thanks once again. regards, sammy Ian...
Hello group members I have a 4 target RF and DC magnetron sputtering system. Both Target and substrate holder can be rotated. The rf cable used is not very ...
We have coated air craft blades with ebeam, You need light heat and rf bias on the holder with the proper process you can coat a 1 mil coating which will take...
Galco123@...
Dec 4, 2005 4:43 pm
2529
Yash, The RF cable is coaxial coaxial. For your rotating requirement, you can consider coil the RF cable into couple turn aact as a buffer when it rotate....
Dear Joan, What sort of deposition speeds are you looking for? When you deposit AlOx,.. When using sputtering,.. Are you using any feedback control in your...
Hi, I assume that you have already contacted your RF matching box & power supply manufacturers (AE, Huettinger, ENI,...) those would be the first port of call....
Dear Joan We are able to deposit such thick and dense aluminum oxide layer using plasma activated electron beam evaporation with very high rates till 100...
Dear all, I need informations about analytic methods for complexes ions (Nb- Chlorides), as well as, Thermodynamic data of them. Thank you Luiz de Miranda -- ...
Luiz Roberto Martins ...
miranda@...
Dec 5, 2005 4:22 pm
2535
10Th Portuguese Conferences on Fracture 10as JORNADAS DE FRACTURA 22-24 February 2006 UNIVERSIDADE DO MINHO Escola de Engenharia, Campus de Azurém, GUIMARÃES...
Dear Sirs, The International Conference on Electron Beam Technology (EBT 2006 ) will held in Varna, Bulgaria (just on the seaside of Black See) in the next...
mladenov@...
Dec 5, 2005 4:32 pm
2537
Congratulations to our colleague Prof. Dr. Stan Veprek who was awarded with the John A. Thornton Memorial Award 2005. John A. Thornton Memorial Award Stan...
Does anybody here in US have diffusion pump DIP3000 (Leybold)with DIN inlet flange - used, rebuilt, but in good working conditions? Even body and jet system...
Ion assisted PVD can be done relatively quickly, around 20 Angstroms per second. The films should be dense, not porus and work well. [Non-text portions of...
dmorton@...
Dec 6, 2005 11:44 pm
2540
Dear Vladimir Chutko, Kinndly visit www.vacuumsys.com Vacuum El systems Ltd is manufacturing DIP 3000. Regards, Xavier...
Xavier palatty
vacuumcal@...
Dec 8, 2005 3:11 pm
2541
********** CALL FOR PAPERS ******** “NanoTrends” Journal invites papers on NanoScience & NanoTechnology The papers are invited from the areas of...
I make thin film solar cell with amorphous silicon. At the top of the solar cell we deposit à layer of Al with a sputtering machine (MRC 903). Actually we...
Dear All Can any one suggest the suitable power supply for for MoS2 based sputter coating. Does it require Pulsed DC power supply or is it possible with normal...
Jacques You may have a water leak or other dirt on the target or inside the chamber. Bernd Meyer ... Von: PVD_coatings@yahoogroups.com ...
bmeyer@...
Dec 10, 2005 1:41 am
2545
Dear Jacques, Probably you use highly unbalanced magnetron cathode, which ensures high electron and ion bombardment of your insulating substrates, but the ...
Dear Soumya, It is much better to use MF pulsed DC power supply for sputtering of MoS2 target. We can supply appropriate. Best regards Milko Angelov ... From:...
Hello everybody! I am a new one to this forum. It is so wonderful to have this exchange of information. My group (Thin Films and Photonics Research Group ) is ...
Pandurang Ashrit
ashritp@...
Dec 10, 2005 5:13 pm
2548
Gentlemen: If I wanted to deposit a shiny, opaque gold film onto paper or plastic, for display purposes (no requirement for purity or uniformity), would I be...
Dear All Following I want to inform you about an interesting conference The 6th International Conference on Coatings on Glass will be held in Dresden in June...
... You can sputter gold in air which will also oxidize any hydrocarbon backstreaming. Don Mattox ... -- ____________________________________ Donald M. Mattox ...