Hello Mr. Roeder, We, the company Hilberg & Partner GmbH, are manufacturing special power amplifiers, up to 10kHz, for the deflection of electron beam guns. If...
Hello Everyone I would like to measure the sputtering target temperature accurately(Approx within few degrees) what is the best method. Thanks in advance. ...
Welcome to MIICS2006 The 3rd Mikkeli International Industrial Coating Seminar 16-18.3.2006 in Mikkeli, Finland. The aim of the seminar is to bring together...
Paavo Ripatti
paavo.ripatti@...
Mar 2, 2006 2:45 pm
2874
Dear all, I was wondering if it was conceivable to achieve reactive deposition of metals oxide (like TiO) by electron beam (by injecting oxygen nearby the ...
Dear All, We want to prepare adherent DLC coatings onto titanium alloys substrates by MS and PECVD for hemocompatible applications. We have tested a graded...
constantin morosanu
cosmorosanu@...
Mar 2, 2006 2:46 pm
2876
... From: "aseva" <aseva@...> To: <vteixeira2000@...>; <vasco@...> Sent: Monday, February 27, 2006 12:43 PM Subject: jpg...
Vasco Teixeira
vasco@...
Mar 2, 2006 2:46 pm
2877
I've not yet done much of a literature search on this, but can anyone suggest a good method for putting Gold contacts on ITO, preferably a method which can be...
CALL FOR PAPERS - Diamond 2006 17th European Conference on Diamond, Diamond-like Materials, Carbon Nanotubes and Nitrides 3-8 September 2006 - Estoril,...
Vasco Teixeira
vasco@...
Mar 2, 2006 2:54 pm
2879
It will work fine to introduce oxygen almost anywhere in the chamber. Doing so close to the E-gun should be no problem as long as the amount of oxygen is not...
dmorton@...
Mar 4, 2006 3:42 pm
2880
The method you suggest should produce some oxide film, but I believe it will be difficult to achieve a "pure" TiO film. Titanium is a natural "getter"...
Dear Pace, We are developing reactive deposition processes with electron beam evaporation and magnetron sputtering (especially also TiO2). We can deposit these...
Hello Pace, Yes this is perfectly possible and is used routinely in optical coating manufacture. Points to watch are the absorption level in the oxide and...
Dear Constantin, As I understood, you use PECVD to deposit the final DLC onto graded Ti-a:C layer. But you must have in mind, that if the substrate temperature...
Hello Safaraz, We regularly use flow controllers to introduce controlled amounts of water vapour into a chamber to control the stress in evaporated layers. If...
Hi, What I have seen most is to "silk-screen" or paint a silver epoxy paste on to of ITO. What you can try using either thermal or e-beam is a thin chrome...
Ken, I just would like to say that we always made gold or other metal contacts BEFORE ITO deposition. So we'd used a regular way to deposit metals and then...
Hello Ken, We have used chrome/palladium/gold utilizing e-beam evaporation for a reliable ITO contact. The palladium was used as a common semiconductor...
Dear Ken, A word of caution regarding gold and any unoxidized tin; Au and Sn have a high affinity for each other and will interdiffuse at room temperature....
George Wityak
gwityak@...
Mar 6, 2006 11:44 am
2890
Dear all, Can any body tell me suppliers of PVD coating service (as a job work) for esthetic purpose? To be specific various coatings on Stainless steel...
Sarfaraz, If you have the money, you can use a fiberoptic temperature probe. This has the advantage that the probe is electrically isolated from the...
Pace Sergio, One of the difficulties of producing TiO2 by reactive evaporation is that there is a tradeoff between the absorption coefficient of the...
How are you attempting to create tin? Process changes from sputter-arc source etc. Marion Shafer [Non-text portions of this message have been removed]...
Galco123@...
Mar 7, 2006 10:09 am
2895
For those interested in TiO2 deposition, they might want to look at: "Achieving Stable Results with Titanium Dioxide," Proc. Soc. Vac. Coaters, 39, p207-210...
Ron Willey
rwilley@...
Mar 7, 2006 10:10 am
2896
We are looking for a low cost substrate heater with the following specification for a laser deposition system. 1. Heating 850 to 900 deg C 2. Cooling 3. X, Y...
November, 15-16 and 17th, 2006 SURMAT 06 - New Challenges in Surface Treatment LES DEFIS DES TRAITEMENTS DE SURFACE 15.16 et 17 Novembre 2006 Colloque Espace...
Dear Adil, we have developed and producing PLD and hybrid PLD & laser systems. Our equipment and more then 20 years experience are available to help solve your...
Multicoats Ltd.
office@...
Mar 8, 2006 2:36 pm
2899
4th International Conference on Hot-Wire CVD (Cat-CVD) Process October 4 - 8, 2006 Takayama, Gifu, Japan http://www1.gifu-u.ac.jp/~hwcvd/index.html Topics ...
Having problems with message search?
Fill out this form to ensure your group is one of the first to be migrated to the new message search system.