You may be better of switching from dc to rf and taking the magnet out. An rf non-magnetron planar diode will have no reasonable restriction on target...
to: lucky.sputter Would you kindly inform me what means quantitatively "Deposition rate will be a little lower, ..." ? Thank you in advance. G. Blasek ... ...
That's a good suggestion, but you require not only an "..rf supply (500 watts should be big enough) and matching network", but a sputter source designed to...
Dear all Please find below this Workshop annoucement. Regards Vasco ... Vasco Teixeira Editor of Journal of Nano Research Journal of Nano Research, JNanoR ...
Vasco Teixeira
vasco@...
Dec 3, 2007 1:04 am
4243
Hi all,I did a experiment that coated Al on PC+ABS and take the samples to QUV test,but after the test,the Al film disappeared.I don't kown the result.Please...
Fu, how thick was your Aluminum film to start with ? UV stimulated oxidation of Aluminum tends to generate thicker oxides than natural oxidation which...
jkools@...
Dec 4, 2007 1:41 am
4245
Yes it can happen. What grade of Al did you use? Also please check if you had IPA in the formulation. Also, excess addition of pearl pigments can bring that...
Quantitatively, I'm not sure. Typially lower by about 50%, but dep rate is a function of yield and scattering, so a magnetron operating at higher pressure may...
I guess the feedthrough could be a concern, though I have had no trouble just clamping the rf power strap to one of the metal water tubes. Most magnetrons have...
Wasa and Hayakawa: http://www.williamandrew.com/title.php?id=142 Excellent overview, and good detail sections. Also, you may like Vossen & Kern. Just google...
Dear members, I need now the User Guide for Leybold trivac D 16 A pump. Can somebody help me with an electronic form of this document? -- Regards, Andrii...
... Rf diode (without magnets) deposition rate at 13.56 MHz is approx. 10% of DC magnetron rate (for a nonmagnetic, conducting target material). Regards Roland...
... But they can have a big capacitance causing huge rf currents which heat up your matchbox and drop down efficiency to zero. Furthermore, they do typically...
You say "I guess the feedthrough could be a concern, though I have had no trouble just clamping the rf power strap to one of the metal water tubes. Most...
________________________________ De: Second International Conference on Advanced Nano Materials (ANM 2008) [mailto:anm2008@...] Enviada: ter 04-12-2007...
Vasco Manuel Pinto Te...
vasco@...
Dec 4, 2007 4:33 pm
4254
Roland: why compare apples and oranges; i.e. "a nonmagnetic, conducting target material" to Ni? Non-magnetic materials are not the issue. Until the magnetic...
Stan: you say, "I can't imagine how the matching network can maintain decent forward power, and worst of all, the tubing inside the chamber will glow,...
Does anyone have experience with thick Ru evaporation? We are using a CHA Mark50 and have problems with the film getting unstable and spattering. We are trying...
I have lots of used ZrB2 targets, and want to do with it. But it's hard and melt point is ver high. So we cann't used it again. Any body have idears? Jerry...
Hi all I have a question that: We did NCVM process for QUV test and we use different PVD film(Al 99.99%,Sn-In Alloy 99.5%,SST).The following is our process: ...
crush, mill, remake things regards ... Dr. ( Mrs.) S. K. Mishra Scientist EII MST Division National Metallurgical Laboratory Jamshedpur, India-831007 ...
Hi everyone, Could you give me information about the major suppliers of in-line PVD coating systems? Particularly decorative coatings for temperature ...
Hi Mark: just read your email. My name is Thomas Schmidt and I am in charge of hard material coating related projects here with VTD VAKUUMTECHNIK DRESDEN /...
Schmidt, Thomas
thomas.schmidt@...
Dec 6, 2007 10:15 pm
4264
Thanks your advice! Jerry ... www.china-raremetal.com Tel:0086-791-8101311 Fax:0086-791-8101211 ... From: Suman Mishra (pathak) To:...
________________________________ De: AMME Autoreply [mailto:AMME.Autoreply@...] Enviada: sex 07-12-2007 13:37 Assunto: FW: Invitation to AMME'2008...
On behalf of Prof Les...
vasco@...
Dec 7, 2007 5:08 pm
4266
Dear All: I am using an e-beam in order to evaporate certain metals and I would like to know if somebody knows if it is possible to use a low pressure ...
Jose
xoarfer@...
Dec 7, 2007 5:08 pm
4267
Yes provided that it is 100% hydrogen and NO oxygen. The explosion limits for H2 / O2 are very broad. For pressures higher than 10-4 see US patent 6,476 340. ...