Hello, I am designing a optical prism / light-pipe and need a45deg surface to reflect the light as it passes thru the plasticmaterial (polycarb or acrylic)...
I am sure the coating for the PC or Acrylic is straight forward. But be careful with the SLA! You will have to preclean these very good. There is all kinds...
Gagnon, Paul E
gagnonpe@...
Feb 4, 2008 2:24 pm
4407
Dear all, We deposited Indium Tin Oxide thin films by Ebeam evaporation. Thermally treated layers have higher transparency and almost higher conductivity, but...
Tim, Aluminum is typically used for reflecting visible light. We are currently running production light pipes and we can help you with that here at Vacucoat...
Martin Goldsberry
mgoldsberry@...
Feb 4, 2008 2:24 pm
4409
Hallo Tim, we are specialized in optical coating on plastics. Please sent me the specification (optical, material, sizes, environmental conditions). best...
Ulrike Schulz
ulrike.schulz@...
Feb 4, 2008 2:25 pm
4410
Hi, You could try to contact Don Parent from D2 Inline solutions they have great experience in integrating coating process onto mold injected plastic parts. ...
Hi Thin film Uniformity and Roughness are 2 separated problem. What is your exact problem? in case of uniformity: you shoul use suitable Corrector shield in...
Hi Thanks for your attention, Although I have the uniformity problem, the main problem is roughness of ITO films. I search for a material like PEDOT:PSS which...
Sara, There has been a lot of work done on "planarizing" substrates to reduce the roughness, especially in the flex display industry. DuPont has developed a ...
Dear All Do you no the chemical composition of "Transparency Paper"? Is the "Transparency Paper" some kine of "polyethylenetetraphthalate"? Sincerely yours ...
sodky abolila
abo_95@...
Feb 10, 2008 10:56 pm
4416
Yes. Some (but not all) transparency films are PET. You can tell with a simple atr-FTIR experiment....
Don Land
dpland@...
Feb 11, 2008 11:37 am
4417
The 4th Mikkeli International Industrial Coating Seminar 27.-29.3.2008 The Seminar brings together representatives from industry and academia to discuss...
Paavo Ripatti
paavo.ripatti@...
Feb 11, 2008 11:38 am
4418
Micro- and Nanotechnologies for Industrial Applications 27th March 2008 In the frame of the FP 6 CA IIPMMAN Project (Improvement of Industrial Production...
Ana Maria Cabral
AMCabral@...
Feb 11, 2008 11:38 am
4419
The Timken Company is looking for potential suppliers to apply Ag coatings (usually less than 100nm thick) to precision bearing balls (usually less than 7mm in...
The Timken Company is currently seeking to add a position in the area of Surface Engineering, with a specific focus on the research and development of...
Hello, This email message is a notification to let you know that a file has been uploaded to the Files area of the PVD_coatings group. File :...
PVD_coatings@yahoogro...
Feb 11, 2008 4:51 pm
4422
Dear Colleagues, It is our great pleasure to solicit your participation at the 5th Symposium on Functional Coatings and Surface Engineering (FCSE-2008) that...
Ludvik Martinu
ludvik.martinu@...
Feb 11, 2008 4:59 pm
4423
Dear all, If anyone is interested in disposing their old secondhand PVD coating machine, I am interested in the same. Kindly contact me with the details. Best...
R Sridhar
srisri@...
Feb 12, 2008 7:06 pm
4424
Dear colleagues: We are pleased to announce the joint 7th Iberian Vacuum Meeting (IVM-7) and 5th European Topical Conference on Hard Coatings (ETCHC-5) to be...
Orlando Teodoro
odt@...
Feb 12, 2008 7:06 pm
4425
Dear All, 1.Let me know the reason why adhesion is comparably poor in Electron beam evaporation than DC magnetron sputtering. 2.Will the sputtered molecule get...
Hello Mr. R Sridha, The company Onlink Technologies in Germany has an used PVD Coating machine. If you are interested in more details please visit the...
We are having problems with curvature developing in our Cu backing plates. The magnetrons are 46" by 6" and the curvature in the Cu backing plate is large...
Dear Steve, One of the issues with copper is that the backing plate may be made with material having slight temper in it. This is often done with copper plate...
George Wityak
gwityak@...
Feb 14, 2008 9:37 pm
4429
Dear Mr. Sridar, I would like to ask you contact me personally trpcevska@... ... From: R Sridhar To: PVD_coatings@yahoogroups.com Sent: Tuesday, February...
Jarka Trpcevska
jarmila.trpcevska@...
Feb 15, 2008 10:30 pm
4430
We do Ion Plating of various coatings like TiN, TiC, etc. on Stainless Steel substrates. We have been noticing frequent peel-off of coating on a fully buffed...
The 4th Mikkeli International Industrial Coating Seminar 27.-29.3.2008 The Seminar brings together representatives from industry and academia to discuss...
paavo.ripatti@...
Feb 15, 2008 10:32 pm
4432
Dear All Re: Fifth HIPIMS Conference to be held on 8th & 9th July, in Venlo, The Netherlands. We are pleased to announce the Fifth HIPIMS Conference to be held...
Having problems with message search?
Fill out this form to ensure your group is one of the first to be migrated to the new message search system.