Dmitri, First you need a signal from the Mark II whether its ion beam is on or off. That signal must come from the Mark II Controller. It depends upon which...
BOTH HAVE REMOTE ON-OFF(series the two together,Or if you have a plc on your machine, set a logic string and place any conditions you wish to a start ...
Galco123@...
Aug 8, 2008 12:07 am
4808
I found this: http://www.ryscor.com/2090.html Stan ... From: Subir Ghosh [mailto:sghosh@...] Sent: Wednesday, July 30, 2008 06:07 AM To:...
Dear Colleagues I have solid dish end cylinder made of mild steel material. The dish end rests at flat “L” shape strip made of stainless steel. Rest of...
Respected sir, I am doing Ph.D research work in semiconducting nanoparticles. I wish to analyze the gas sensing properties for my samples. I humbly request you...
kitcha kumar
tkrishnakumar_nano@...
Aug 8, 2008 12:10 am
4812
Congratulation to Dr. Fortunato and members. However, there is some question on the thermal stability of paper FET. We know that the paper tend to degrade with...
Has anyone used DC magnetron for Tungsten Carbide films? We are thinking of doing this but the only references I can find involve RF. Thanks, Greg [Non-text...
... I do research in preparation of ZnO-based thin films , Is there any capability to make some TEM by your help ? If yes , how can it be possible? Best...
Dear everyone, I am facing problem in managing the color of TiN. My coating is OK but there is a variation of color. Sometimes it very Light color and ...
Dear everyone, Can anybody tell me the complete information of DLC Coating by Cathodic Arc evaporation in PVD? I would like to know that: - How it works? -...
Look for articles under "FCVA". Look up Nanofilms Technologies International, Singapore. I met the CEO, Dr. Xu last week, his PhD was in "DLC by FCVA". Work...
Dear Mr. Mirza, For deposition of ta-C coatings by cathodic arc, please look at the papers of Prof. Beng Kang Tay (just type his name on searching tool you...
Dear Mr. Mirza, If you applied the same parameters for two batches of deposition and saw the difference in coating color, please check the base pressure of...
Dear. Shoaibmirza I will inform you my thought if you will consider.. you must refer it and check... i think the varivable color is coated by same process but...
Dear Shoaibmirza, If your TiN color is getting darker from cycle to cycle, in my experience, this is caused by buildup of coating on the chamber walls that...
Dear Shoaibmirza: The color of TiN coatings depends on nitrogen content. Can go from silvery metallic to brown. Even with controlled parameters the nitrogen...
Dear All, We have a cylindrical box chamber for optical coating(h1100mm*d900mm). We want to electroplate that for cleaning,please guide me ,and if you have,...
Dear Shoaibmirza, The colour balance can be related to the stoichiometry of the metal and nitrogen. I don't know if your process is sputtering, arc or...
Dermot Monaghan
dermot.monaghan@...
Aug 11, 2008 6:54 pm
4828
Here you go, http://www.crystallography.net/ http://rruff.geo.arizona.edu/AMS/amcsd.php These are free but limited. If you are looking for something specific...
Dear Shoaibmirza, Cathodic Arc DLC requires more specialized equipment than metal coating because of the difficulty in controlling the arc motion. Also, a...
Hi Greg, WC can be sputtered with DC, quite a common process for low friction functional coatings. Normally the WC has a cobalt or nickel binder. ...
Dermot Monaghan
dermot.monaghan@...
Aug 11, 2008 7:04 pm
4831
Dear Friends I have same question as Mr. Mirza e-mail, but for PVD (Physical vapor deposition) Method. I have Bak760 Balzers coating machine with 2 e-gun...
PhD Mohaghan, Have you ever had problem with WC targets cracking in process? It is a concern. The binder is cobalt, roughly 3-4%. Regards, Greg ... [Non-text...
Shoaibmirza: The Ti film is silvery-gray until enough nitrogen reacts with it during growth to change the color. If the TiN film is a lower- density columnar...
Hello everyone, I'm trying to deposit oxide and nitride films by reactive sputtering of metal targets. I've read many papers on the subject and the most cost ...
Haloo Everyone, Do you have any suggestion for heatinf in presence of strong electric field. I need to heat my substrate at around 400-500 C while it is in...