Dear Mr. Milko, I am using cathodic arc evaporation method in PVD. My substrate temperature is 180 to 200 C during deposition. I am doing decorative coatings...
Hello I didn't thank enough the people who sent in their options and feedback on the PECVD process, it was much appreciated.I am still doing my research as...
Brass has Zn in it, nasty stuff, use bronze, CuAl8 ,if you are looking for a gold color or go to TiN or ZrN reactively. ________________________________ From:...
Does anybody know where I can buy the 4 inch IC tray with 64 pockets (10mmx10mm), part number: H44-360 that is manufactured by Fluoroware Inc. Thanks Vinay ...
We are looking for Technology for Multi-layered Aluminium Moly coating with varying moly% by magnetron sputtering. The substrate is Steel AISI 4340 heat...
This is probably for preform type, high end parts. Depending on the wafer size, we can sputter. We also have ebeam codep but believe the most consistant is...
Galco123@...
Jun 8, 2009 2:50 pm
5358
Dear PVD coatings group, I send you this message because I am looking for a postdoctoral position candidate before beginning of July. I send you the detailed...
NOUVEAU Corinne
corinne.nouveau@...
Jun 8, 2009 2:51 pm
5359
Tim: PlascoatR is an in-chamber pre-treatment process and top-coating process to prevent environmental tarnishing/spoiling of the metal film. The PlascoatR...
Hi All, I am trying to deposit a thick (10-20micron) layer of InSn (52% In 48% Sn, 118oC melt point) from a metal target of the alloy by magnetron sputtering....
Dear Shoaib mirza, First of all, I mean, you have to start ion etch cleaning after reaching at leats 1exp-2 Pa, 2exp-3 Pa is better. Next is the substrate...
gold plus aluminum plus a little silicon = purple (google "purple plague") ... From: dian_nataliez [mailto:dian_nataliez@...] Sent: Thursday, June 4,...
Dear Ramachandra: We have a (4) four cathode R&D system (cryo and turbo pumped, oil free), with at least two cathodes outfitted for Mo and Al. Please contact...
Dear Dian, You can try gold sputtered onto aluminum or a gold-aluminum alloy. Thanks, George ________________________________ From:...
George Wityak
gwityak@...
Jun 9, 2009 3:05 pm
5365
For all: Natel.com is actually _http://www.natelengr.com/_ (http://www.natelengr.com/) Regards, PVD Plasma [Non-text portions of this message have been...
Dear Ramachandra, Please, kindly let us know, what kind of equipment you are looking for - research or industrial scale? What are the substrate dimensions, two...
Dear colleagues, I am interested in purchasing a furnace type thermal CVD system for nanostructure fabrication. Please forward me information from vendors that...
Steve: After I wrote my first reply, I remembered you said you were trying to deposit a 10 to 20 micron film! I went back to see the dep rate. You report it as...
Steve It's situations like these when an RGA is most usefull. It would help you determine the source of the oxygen. The first thing I would do is to use one to...
Dear Mr.Ramachandra, Could tell me more about your requirement? Size and shape of the substrates, quantity/ the number of substrates to be coated, layer...
I'm looking for ideal cathodic arc deposition conditions for CrN (with chrome inter-layers)? How does CrN cathodic arc deposition differ from TiN deposition?...
Dear Milko, First of all thanks for the reply. Please tell me that after coating pure Ti for 7 min in the presence of Argon gas, should i coat TiC in the...
Dear Steve, Stan, My suggestion is to use DC sputtering and to increase the deposition rate at least up to 500 nm/min. Best regards, Milko ... From:...
We need a UV lamp that can provide UV light of wavelength 180 nm to 250 nm. The narrow light spot just to illuminate the 2 cm x 2 cm sample area is preferred....
Dear Jeremiah, The undisputed leader in CVD systems is Ionbond AG Olten and the website is www.ionbond.com I am responsible for equipment sales in North...
Dear Shoaib mirza, It is not necessary to use Ar during the deposition. Regarding the Acetylene partial pressure - it depends on the system configuration,...